Hot corrosion effect of the vacuum arc melted (a2/γ)Ti-48Al-2Nb-0.7Cr-0.3Si alloy under an environment of NaCl-Na2SO4 salt
The Ti-48Al-2Nb-0.7Cr-0.3Si alloy comprising of α2-Ti3Al and γ-TiAl phases was successfully fabricated using vacuum arc melting. To study its hot corrosion behaviour, the alloy was subjected to cyclic thermal loading under a Na2SO4 + 25wt.%NaCl molten salt mixture at 900 °C for up to 60 h. Mass chan...