Study on LBE corrosion failure of FeAl/Al2O3 coatings after ion irradiation

FeAl/Al2O3 coatings, candidate coating materials for lead-cooled fast reactors, are first irradiated to produce pre-defects and then subjected to lead-bismuth eutectic corrosion to simulate the performance in the coupled field of irradiation and corrosion. Irradiation causes voids in the outer Al2O3...

Descripción completa

Detalles Bibliográficos

Autores principales:	Yilong Zhong, Wei Zhang, Jian Yang, Liqiu Yong, Qingyu Li, Yuntai Luo, Yi Zhou, Yuanjie Fu, Ning Liu, Xi Qiu, Jijun Yang
Formato:	Artigo
Lenguaje:	Inglês
Publicado:	Elsevier 2024-06-01
Colección:	Materials & Design
Materias:	FeAl/Al2O3 coatings Irradiation effect Lead-bismuth eutectic (LBE) Irradiation-corrosion
Acceso en línea:	http://www.sciencedirect.com/science/article/pii/S0264127524003939
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!