Study on LBE corrosion failure of FeAl/Al2O3 coatings after ion irradiation

FeAl/Al2O3 coatings, candidate coating materials for lead-cooled fast reactors, are first irradiated to produce pre-defects and then subjected to lead-bismuth eutectic corrosion to simulate the performance in the coupled field of irradiation and corrosion. Irradiation causes voids in the outer Al2O3...