Secondary Phase Interaction at Interfaces of High-Strength Brazed Joints made using Liquid Phase Sintered Alumina Ceramics and Ag-Cu-Ti Braze Alloys
Alumina-to-alumina brazed joints were formed using 96.0 and 99.7 wt.% Al(2)O(3) ceramics using 150 µm thick Ticusil(®) (68.8Ag-26.7Cu-4.7 wt.% Ti) braze preforms. Brazing was conducted in a vacuum of 1 × 10(−5) mbar at 850 °C for 10 minutes. Joint strengths were evaluated using four-point bend testi...