Effect of Cu Additions on the Evolution of Eta-prime Precipitates in Aged AA 7075 Al–Zn–Mg–Cu Alloys

In the present study, after solid solution treatment, four different artificial aging treatments (100, 120, 140 and 160 °C) were performed on Al-5.98Zn-2.86Mg-1.61Cu (wt.%) alloy, denoted as 7075-LCu, and Al-5.91Zn-2.83Mg-1.98Cu (wt.%) alloy, denoted as 7075-HCu. Peak aging conditions were determine...