Study on Microstructure of He+-irradiation Induced Defects in Tungsten
The samples of tungsten were irradiated by 100keV helium ions at room temperature with different fluences ranging from 1.4×1017-3.5×1017/cm2 and then annealed at 1100℃. The interaction of helium-related defects with helium fluence was studied by means of X-ray diffraction (XRD), slow positron beam a...