Failure Analysis of Corrosion-Induced Perforation in B10 Copper-Nickel Alloy Pipelines
The B10 copper-nickel alloy pipeline used for seawater transportation on a certain platform was found to have corrosion perforation at the weld joint between the elbow and the flange during a shutdown inspection.In this study， the failure mechanism of corrosion perforation was analyzed using macrosc...