High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment
High temperature corrosion and stress corrosion cracking of 310S austenitic stainless steel in wet chloride environment at a high temperature was investigated. The result showed that high temperature corrosion products mostly consisted of ferrous oxides and chromium oxides. Chloride ions attacked a...