Hydrogen-Induced Cracking in CGHAZ of Welded X80 Steel under Tension Load

X80 steel is extensively used in hydrogen environments and is susceptible to hydrogen embrittlement (HE). This paper studied the hydrogen-induced cracking (HIC) behavior in the coarse-grained heat-affected zone (CGHAZ) of X80 steel welds, through applying in situ hydrogen-charging tensile experiment...

ver descrição completa

Na minha lista:
Principais autores: Jinxin Gou, Xiao Xing, Gan Cui, Zili Li, Jianguo Liu, Xiangyuan Deng
Formato: Artigo
Idioma:Inglês
Publicado em: MDPI AG 2023-07-01
coleção:Metals
Assuntos:
carbon steel
tensile
hydrogen diffusion
SEM
hydrogen embrittlement
Acesso em linha:https://www.mdpi.com/2075-4701/13/7/1325