Formation and Dissolution of γ’ Precipitates in IN792 Superalloy at Elevated Temperatures
Precipitation of γ’ phase in nickel-base superalloy IN792-5A was studied using in-situ Small Angle Neutron Scattering (SANS). It was found that additional precipitates are formed after reheating above 600 °C when the material is previously fast cooled (100 K/min) from 900 °C. The size distribution a...