Superhydrophobic fluoride conversion coating on bioresorbable magnesium alloy – fabrication, characterization, degradation and cytocompatibility with BMSCs

A micro-nano structure CaF2 chemical conversion layer was prepared on fluoride-treated AZ31 alloy, then the composite fluoride conversion film (CaF2/MgF2) was modified by stearic acid (SA) and fabricated a superhydrophobic surface. The fluoride-treated magnesium, fluoride conversion film and superhy...