Cracking suppression in powder bed fusion-laser beam of CM247LC Ni-based superalloy
High γ′ Ni-based superalloys, such as CM247LC studied here, suffer from a high propensity for crack formation during additive manufacturing, hampering mission-critical applications due to poor weldability. In this work, crack suppression was achieved in CM247LC processed via Powder Bed Fusion-Laser...