An interface shear damage model of chromium coating/steel substrate under thermal erosion load
The Cr-plated coating inside a gun barrel can effectively improve the barrel’s erosion resistance and thus increase the service life. However, due to the cyclic thermal load caused by high-temperature gunpowder, micro-element damage tends to occur within the Cr coating/steel substrate interface, lea...