Effect of Nitrogen Content on Behavior of Elevated Temperature Deformation of Austenite Stainless Steel 1Cr17Mn6Ni5N
The test steel 1Cr17Mn6Ni5N (/% ： 0. 09 ~ 0.11C, 0.19 ~ 0.29Si, 7.33~7.42Mn, 0.011 -0.015P, 0. 004 ~ 0. 007S, 16. 87 ~ 17. 24Cr, 5. 06 ~5.19Ni, 0. 21 ~0. 40N) is melted by a 10 kg vacuum induction furnace with adding chromium nitride to N-alloying in nitrogen atmosphere. The compression 60% experime...