Synergistic damage behavior of He ion irradiation and molten salt corrosion in SiC at 750 °C

CVD SiC samples exposed to 400 keV He ion irradiation at 750 °C were subsequently corroded in FLiNaK molten salt at 750 °C for 166 h. After corrosion, the dissolution of Si led to the formation of a carbon-rich layer and obvious denudation of the SiC. The microstructure of the C-rich layer was first...