Fatigue Crack Growth Behavior and Failure Mechanism of Nickel-Based Alloy GH4169 under Biaxial Load Based on Fatigue Test of Cruciform Specimen
Due to the complex geometry and various cyclic loads, aeroengine components are often in a multiaxial complex stress state during service. Multiaxial fatigue is a major cause of many air accidents. It is of great significance to study the fatigue failure mechanism of aeronautical materials. This pap...