Evolution of the precursor structure during the preparation of the nanopowders with perovskite-type LnLn’O3 (Ln, Ln’ = REE) complex oxide phase in the La2O3-Lu2O3-Yb2O3 system

The thermal decomposition of complex oxide phases, such as perovskite, in the La2O3-Lu2O3-Yb2O3 systemwith a specific surface area of 37 m2/g, synthesised by the heterogeneous precipitation method under non-isothermal conditions of linear heating at a rate of 5 deg/min, was studied to reveal the fea...