Crack Initiation in Ni-Based Single Crystal Superalloy under Low-Cycle Fatigue-Oxidation Conditions
The mechanism of oxidation-assisted initiation of surface cracks of a fourth-generation Ni-based single crystal superalloy was systematically investigated during low cycle fatigue at 900 °C and 980 °C. The results show that cracks initiate near the surface defects at 900 °C, while they initiate in t...