Effect of nonmetallic inclusions on steel welds metal hot cracking
Intercrystally distributed nonmetallic inclusions greatly increase weld susceptibility to hot cracking. Oxide and sulphide inclusions are the result of contaminated base material or its highly oxidised surfaces and they can be a consequence of metallurgical reactions between welding slag and remelte...